ZT 154 is a dispersant with good dispersancy at low temperature, good detergency and chlorine free.
It is made from high active polyisobutylene by thermal adduction process. It can inhibit carbon deposition
and paint film formation on engine position.
Product Applications:
It is mainly used for blending low and middle grade engine oil and it also can be used for petrochemical aid
and fuel detergent.
Product Feature:
Good dispersancy at low temperature
Good detergency
Chlorine free
Quality Specification:
Item | Specification | Test Method |
Appearance | Viscous transparent liquid | Visual |
Density(20℃), kg/m³ | 890-950 | NB/SH/T 0870, ASTM D7042 |
Color(D), Scale | ≤3.5 | GB/T 6540 |
Flash Point(COC, ℃) | ≥180 | GB/T 3536, ASTM D92 |
Kinematic Viscosity(100℃), mm2/s | ≥150 | NB/SH/T 0870, ASTM D7042 |
TBN, mg KOH/g | 15-25 | SH/T 0251, ASTM D2896 |
Nitrogen, %(m/m) | 1.0-1.25 | NB/SH/T 0704, ASTM D5762 |
Water, %(m/m) | ≤0.08 | GB/T 260, ASTM D95 |
Mechanical Impurities | ≤0.08 | GB/T 511 |
Packing and Disposal
Pls store in dry, clean, ventilated warehouse.
Suggestion: The highest storage temperature shall not exceed 65℃, and for long-term storage shall not exceed 45 ℃.
For product details of safety pls refer to the MSDS of this product.
ZT77208 is a premium-grade gear oil compound meticulously crafted to excel in extreme pressure (EP) and high-load conditions. Its advanced formulation combines superior base oils with a high-performance additive package, ensuring optimal lubrication and protection for gears, bearings, and transmission systems. With a yellow transparent liquid appearance , this compound adheres to stringent quality benchmarks, including phosphorus content exceeding 1.00% (w/w) and sulfur content surpassing 30.00% (w/w) . These high levels of sulfur and phosphorus additives form a robust protective film on metal surfaces, reducing friction, wear, and corrosion even under severe operational stress .