ZT79977 This product is light in color, more stable in hard water, lubricating, good cleaning, and has good rust prevention, corrosion prevention, no pollution in the use of fabric, does not affect the dyeing, long service life.
| Availability: | |
|---|---|
| Quantity: | |
ZT 79977
Knitting emulsified oil compound agent
Product Instruction:
ZT79977 This product is light in color, more stable in hard water, lubricating, good cleaning, and has good rust prevention, corrosion prevention, no pollution in the use of fabric, does not affect the dyeing, long service life.
Additive dose:
Performance Level | Dosage (%(w/w)) |
Emulsion type | 5%-10% |
It can be adjusted according to different sources of base oil
Quality Specification:
Item | Specification | Test Method |
Appearance | Transparent liquid | Visual |
Kinematic Viscosity(100℃), mm²/s | Report | GB/T265 |
Flash Point(COC, ℃) | >90 | GB/T3536 |
mechanical impurity,% | <0.05 | GB/T511 |
Moisture,% | <0.03 | GB/T260 |
Packing and Disposal
1. Pls pack in 200kg metal drums or ton drums and store in a dry, clean, ventilated warehouse.
2. Suggestion: The maximum storage temperature should not exceed 65℃, and the long-term storage
should not exceed 45℃ .
3.Safety precautions, please refer to the MSDS of this product.
ZT77208 is a premium-grade gear oil compound meticulously crafted to excel in extreme pressure (EP) and high-load conditions. Its advanced formulation combines superior base oils with a high-performance additive package, ensuring optimal lubrication and protection for gears, bearings, and transmission systems. With a yellow transparent liquid appearance , this compound adheres to stringent quality benchmarks, including phosphorus content exceeding 1.00% (w/w) and sulfur content surpassing 30.00% (w/w) . These high levels of sulfur and phosphorus additives form a robust protective film on metal surfaces, reducing friction, wear, and corrosion even under severe operational stress .